SABIC Innovative Plastics Lexan? DMX6014 PC Copolymer (Asia Pacific) 物性表 物理性能 额定值 (公制) 额定值 (英制) 测试方法 比重 1.15 g/cc 1.15 g/cc ASTM D 792 密度 1.15 g/cc 0.0415 lb/in3 ISO 1183 线性成型收缩率,Flow 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm 0.0050 - 0.0070 in/in @Thickness 0.126 in SABIC Method 熔体流动速率 10 g/10 min @Load 1.20 kg, Temperature 300 °C 10 g/10 min @Load 2.65 lb, Temperature 572 °F [cm^3/10 min] Melt Volume Rate; ISO 1133 12 g/10 min @Load 1.20 kg, Temperature 300 °C 12 g/10 min @Load 2.65 lb, Temperature 572 °F ASTM D 1238 机械性能 额定值 (公制) 额定值 (英制) 测试方法 Hardness, Rockwell L 90 90 ASTM D 785 洛氏硬度(R 级) 117 117 ASTM D 785 抗张强度(断裂) 45.0 MPa 6530 psi Type I, 50 mm/min; ASTM D 638 48.0 MPa 6960 psi 50 mm/min; ISO 527 抗张强度(屈服) 53.0 MPa 7690 psi Type I, 50 mm/min; ASTM D 638 55.0 MPa 7980 psi 50 mm/min; ISO 527 伸长率 (断裂) 45 % 45 % Type I, 50 mm/min; ASTM D 638 50 % 50 % 50 mm/min; ISO 527 屈服伸长率 5.0 % 5.0 % Type I, 50 mm/min; ASTM D 638 5.5 % 5.5 % 50 mm/min; ISO 527 拉伸模量 2.15 GPa 312 ksi 1 mm/min; ISO 527 2.40 GPa 348 ksi 5 mm/min; ASTM D 638 弯曲强度 75.0 MPa 10900 psi 1.3 mm/min, 50 mm span; ASTM D 790 78.0 MPa 11300 psi 2 mm/min; ISO 178 弯曲模量 2.15 GPa 312 ksi 2 mm/min; ISO 178 2.20 GPa 319 ksi 1.3 mm/min, 50 mm span; ASTM D 790 悬壁梁缺口冲击强度 0.700 J/cm @Temperature -30.0 °C 1.31 ft-lb/in @Temperature -22.0 °F ASTM D 256 2.20 J/cm @Temperature 23.0 °C 4.12 ft-lb/in @Temperature 73.4 °F ASTM D 256 10.0 kJ/m2 @Temperature -30.0 °C 4.76 ft-lb/in2 @Temperature -22.0 °F 80*10*3; ISO 180/1A 20.0 kJ/m2 @Temperature 23.0 °C 9.52 ft-lb/in2 @Temperature 73.4 °F 80*10*3; ISO 180/1A 简支梁缺口冲击强度 1.00 J/cm2 @Temperature -30.0 °C 4.76 ft-lb/in2 @Temperature -22.0 °F V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA 2.00 J/cm2 @Temperature 23.0 °C 9.52 ft-lb/in2 @Temperature 73.4 °F V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA 冲击试验 55.0 J 40.6 ft-lb Multiaxial Impact; ISO 6603 电气性能 额定值 (公制) 额定值 (英制) 测试方法 介电常数 2.8 @Frequency 1.00e+6 Hz 2.8 @Frequency 1.00e+6 Hz IEC 60250 3.0 @Frequency 50.0 - 60.0 Hz 3.0 @Frequency 50.0 - 60.0 Hz IEC 60250 3.0 @Frequency 1000 Hz 3.0 @Frequency 1000 Hz IEC 60250 介电强度 35.0 kV/mm @Thickness 1.60 mm 889 kV/in @Thickness 0.0630 in in oil; IEC 60243-1 47.0 kV/mm @Thickness 0.800 mm 1190 kV/in @Thickness 0.0315 in in oil; IEC 60243-1 耗散因数 0.010 @Frequency 1.00e+6 Hz 0.010 @Frequency 1.00e+6 Hz IEC 60250 0.012 @Frequency 1000 Hz 0.012 @Frequency 1000 Hz IEC 60250 0.030 @Frequency 50.0 - 60.0 Hz 0.030 @Frequency 50.0 - 60.0 Hz IEC 60250 热性能 额定值 (公制) 额定值 (英制) 测试方法 Hot Ball Pressure Test <= 100 °C <= 212 °F IEC 60695-10-2 载荷下热变形温度(0.46 MPa) 113 °C 235 °F Edgew 120*10*4 sp=100mm; ISO 75/Be 113 °C @Thickness 3.20 mm 235 °F @Thickness 0.126 in unannealed; ASTM D 648 载荷下热变形温度(1.8 MPa) 95.0 °C 203 °F Flatw 80*10*4 sp=64mm; ISO 75/Af 97.0 °C @Thickness 3.20 mm 207 °F @Thickness 0.126 in unannealed; ASTM D 648 维卡软化温度 113 °C 235 °F Rate B/50; ASTM D 1525 113 °C 235 °F Rate B/50; ISO 306 118 °C 244 °F Rate B/120; ISO 306 可燃性(UL94) HB @Thickness 1.50 mm HB @Thickness 0.0591 in UL 94 HB @Thickness 3.00 mm HB @Thickness 0.118 in 2nd value; UL 94 灼热丝易燃指数 650 °C @Thickness 1.50 mm 1200 °F @Thickness 0.0591 in Glow Wire Flammability Index; IEC 60695-2-12 700 °C @Thickness 3.00 mm 1290 °F @Thickness 0.118 in Glow Wire Ignitability Temperature; IEC 60695-2-13 材料描述 测试方法 Ball Pressure Test, 75°C +/- 2°C pass IEC 60695-10-2 Erichson scratch depth, 6N, micrometer 14 SABIC Method Pencil Hardness test, 1kgf F ASTM D 3363