美国SABIC LEXAN PC DMX6014全国直销

SABIC Innovative Plastics Lexan? DMX6014 PC Copolymer (Asia Pacific) 物性表
物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	1.15 g/cc	1.15 g/cc	ASTM D 792
密度	1.15 g/cc	0.0415 lb/in3	ISO 1183
线性成型收缩率,Flow	0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
0.0050 - 0.0070 in/in
@Thickness 0.126 in
SABIC Method
熔体流动速率	10 g/10 min
@Load 1.20 kg, Temperature 300 °C
10 g/10 min
@Load 2.65 lb, Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
12 g/10 min
@Load 1.20 kg, Temperature 300 °C
12 g/10 min
@Load 2.65 lb, Temperature 572 °F
ASTM D 1238
机械性能	额定值 (公制)	额定值 (英制)	测试方法
Hardness, Rockwell L	90	90	ASTM D 785
洛氏硬度（R 级）	117	117	ASTM D 785
抗张强度(断裂)	45.0 MPa	6530 psi	Type I, 50 mm/min; ASTM D 638
48.0 MPa	6960 psi	50 mm/min; ISO 527
抗张强度(屈服)	53.0 MPa	7690 psi	Type I, 50 mm/min; ASTM D 638
55.0 MPa	7980 psi	50 mm/min; ISO 527
伸长率 (断裂)	45 %	45 %	Type I, 50 mm/min; ASTM D 638
50 %	50 %	50 mm/min; ISO 527
屈服伸长率	5.0 %	5.0 %	Type I, 50 mm/min; ASTM D 638
5.5 %	5.5 %	50 mm/min; ISO 527
拉伸模量	2.15 GPa	312 ksi	1 mm/min; ISO 527
2.40 GPa	348 ksi	5 mm/min; ASTM D 638
弯曲强度	75.0 MPa	10900 psi	1.3 mm/min, 50 mm span; ASTM D 790
78.0 MPa	11300 psi	2 mm/min; ISO 178
弯曲模量	2.15 GPa	312 ksi	2 mm/min; ISO 178
2.20 GPa	319 ksi	1.3 mm/min, 50 mm span; ASTM D 790
悬壁梁缺口冲击强度	0.700 J/cm
@Temperature -30.0 °C
1.31 ft-lb/in
@Temperature -22.0 °F
ASTM D 256
2.20 J/cm
@Temperature 23.0 °C
4.12 ft-lb/in
@Temperature 73.4 °F
ASTM D 256
10.0 kJ/m2
@Temperature -30.0 °C
4.76 ft-lb/in2
@Temperature -22.0 °F
80*10*3; ISO 180/1A
20.0 kJ/m2
@Temperature 23.0 °C
9.52 ft-lb/in2
@Temperature 73.4 °F
80*10*3; ISO 180/1A
简支梁缺口冲击强度	1.00 J/cm2
@Temperature -30.0 °C
4.76 ft-lb/in2
@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
2.00 J/cm2
@Temperature 23.0 °C
9.52 ft-lb/in2
@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
冲击试验	55.0 J	40.6 ft-lb	Multiaxial Impact; ISO 6603
电气性能	额定值 (公制)	额定值 (英制)	测试方法
介电常数	2.8
@Frequency 1.00e+6 Hz
2.8
@Frequency 1.00e+6 Hz
IEC 60250
3.0
@Frequency 50.0 - 60.0 Hz
3.0
@Frequency 50.0 - 60.0 Hz
IEC 60250
3.0
@Frequency 1000 Hz
3.0
@Frequency 1000 Hz
IEC 60250
介电强度	35.0 kV/mm
@Thickness 1.60 mm
889 kV/in
@Thickness 0.0630 in
in oil; IEC 60243-1
47.0 kV/mm
@Thickness 0.800 mm
1190 kV/in
@Thickness 0.0315 in
in oil; IEC 60243-1
耗散因数	0.010
@Frequency 1.00e+6 Hz
0.010
@Frequency 1.00e+6 Hz
IEC 60250
0.012
@Frequency 1000 Hz
0.012
@Frequency 1000 Hz
IEC 60250
0.030
@Frequency 50.0 - 60.0 Hz
0.030
@Frequency 50.0 - 60.0 Hz
IEC 60250
热性能	额定值 (公制)	额定值 (英制)	测试方法
Hot Ball Pressure Test	<= 100 °C	<= 212 °F	IEC 60695-10-2
载荷下热变形温度(0.46 MPa)	113 °C	235 °F	Edgew 120*10*4 sp=100mm; ISO 75/Be
113 °C
@Thickness 3.20 mm
235 °F
@Thickness 0.126 in
unannealed; ASTM D 648
载荷下热变形温度(1.8 MPa)	95.0 °C	203 °F	Flatw 80*10*4 sp=64mm; ISO 75/Af
97.0 °C
@Thickness 3.20 mm
207 °F
@Thickness 0.126 in
unannealed; ASTM D 648
维卡软化温度	113 °C	235 °F	Rate B/50; ASTM D 1525
113 °C	235 °F	Rate B/50; ISO 306
118 °C	244 °F	Rate B/120; ISO 306
可燃性(UL94)	HB
@Thickness 1.50 mm
HB
@Thickness 0.0591 in
UL 94
HB
@Thickness 3.00 mm
HB
@Thickness 0.118 in
2nd value; UL 94
灼热丝易燃指数	650 °C
@Thickness 1.50 mm
1200 °F
@Thickness 0.0591 in
Glow Wire Flammability Index; IEC 60695-2-12
700 °C
@Thickness 3.00 mm
1290 °F
@Thickness 0.118 in
Glow Wire Ignitability Temperature; IEC 60695-2-13
材料描述		测试方法
Ball Pressure Test, 75°C +/- 2°C	pass	IEC 60695-10-2
Erichson scratch depth, 6N, micrometer	14	SABIC Method
Pencil Hardness test, 1kgf	F	ASTM D 3363